ML3075
Technical Parameters
| Unit | Max | Target | Min | Test Method | |
| BASUS WEIGHT | (g/㎡) | 80.0 | 75.0 | 70.0 | GBT 451.2-1989 TAPPI 410 om-2002 |
| Thickness (50 kPa) | (mm) | 0.520 | 0.460 | 0.400 | GB/T 451.3-2002(50kpe) TAPPI 411 om-2015(50kpa) |
@ 5.33 cm/s - 32 L/min | (mm H2O) (Pa) | / / | 1.0 9.8 | / / | ATI-100XP Automated Filter Test |
| Air Permeability | (cfm) | / | 120 | 100 | TAPPL T 251 (125pa) |
| TENSILE STRENGTH一MD: | (kN/m) | / | 1.400 | 0.800 | GB/T 12914-2008 (25.4mm/min) TAPPI 494 om-2013(25.4mm/min) |
| TENSILE STRENGTH-CD: | (kN/m) | / | 0.800 | 0.400 | GB/T 12914-2008 (25.4mm/min) TAPPI 494 om-2013(25.4mm/min) |
| GURLEY STIFFNESS - MD: | (mg) | / | 1020 | 750 | TAPPIT-543-94 |
| Max. Pore Size: | μm | / | 70 | / | QC/T974-2007 ASTM F316-03 |
| EFFICIENCY (BETA-200): | μm | 30 | ISO 16889(test run to 200 kPa) ISO 16889(200 kPa) | ||
| DUAT HOLDING CAPACITY: | (g/㎡) | 140 | ISO 16889(test run to 200 kPa) ISO 16889(200 kPa) |
Technical Parameters
| Unit | Max | Target | Min | Test Method | |
| BASUS WEIGHT | (g/㎡) | 80.0 | 75.0 | 70.0 | GBT 451.2-1989 TAPPI 410 om-2002 |
| Thickness (50 kPa) | (mm) | 0.520 | 0.460 | 0.400 | GB/T 451.3-2002(50kpe) TAPPI 411 om-2015(50kpa) |
@ 5.33 cm/s - 32 L/min | (mm H2O) (Pa) | / / | 1.0 9.8 | / / | ATI-100XP Automated Filter Test |
| Air Permeability | (cfm) | / | 120 | 100 | TAPPL T 251 (125pa) |
| TENSILE STRENGTH一MD: | (kN/m) | / | 1.400 | 0.800 | GB/T 12914-2008 (25.4mm/min) TAPPI 494 om-2013(25.4mm/min) |
| TENSILE STRENGTH-CD: | (kN/m) | / | 0.800 | 0.400 | GB/T 12914-2008 (25.4mm/min) TAPPI 494 om-2013(25.4mm/min) |
| GURLEY STIFFNESS - MD: | (mg) | / | 1020 | 750 | TAPPIT-543-94 |
| Max. Pore Size: | μm | / | 70 | / | QC/T974-2007 ASTM F316-03 |
| EFFICIENCY (BETA-200): | μm | 30 | ISO 16889(test run to 200 kPa) ISO 16889(200 kPa) | ||
| DUAT HOLDING CAPACITY: | (g/㎡) | 140 | ISO 16889(test run to 200 kPa) ISO 16889(200 kPa) |